Stainless steel specialist for static castings.

Our manufacturing process for your requirements.

schmidt-und-clemens-gmbh-und-co-kg-X0A0461.jpg

High-quality stainless steel components in static casting made by S+C.

This is where experiences and skills count.

We at S+C operate an efficient, state-of-the-art stainless steel foundry for static castings. All our materials are available in static casting:

  • Castings with an outer diameter of 30 mm - 2,000 mm.
  • Castings with a weight of up to 3,000 kgs.
  • More than 90 years of experience in static casting.

All our materials are also available for sand casting.

„Made by S+C” also means: we check which manufacturing process and which material is most suitable for your requirement. Our components leave S+C either in as cast / pre-machined condition for finish machining in your factory or as a ready-to-install component. Our products are approved by almost all inspection and quality assurance companies, worldwide.

In order to check in advance how your casting can be optimized, we rely on specialized solidification simulation software. Using this technology, we thus simulate our sand castings in order to provide you with suggestions as to how costs can be saved by modifying the casting, if this should be necessary.

Static casting.

For freedom in design.

We provide 90 years of experience in static casting. Static castings are characterized by freedom of design and geometry.

Casting close to the final shape saves machining operations and costs.

Static casting at a glance:

Experience:
more than 90 years in static casting.

Single part production:
Yes.

Series Production:
Small batch

Manufacturing:
Machining, assembly, welding.

Collaboration:
Full-service partner - R+D, failure analysis, materials + applications consulting, manufacturing, assembly, commissioning, repair.

Technical data:

Static castings
Outer-Ø 30mm - 2,000mm
Length 30mm - 4,500mm
Width 30mm - 2,000mm
Height 1,700mm
Weight (insert/finished) 5,600kg / 3,000kg
*1G corresponds to 1 times the acceleration due to gravity. The G-force acts on the solidifying steel through rotation and influences the microstructure formation during solidification towards better mechanical values.

Products at a glance:

Industries:

Materials:

Centralloy®/ Märker® Material No. Short name Analysis / Guide values in % ≈ASTM
C Cr Ni Mo Other
G 21-02 "Lean Duplex" 1.4162 GX2CrMnNiN21-5-1 0,02 21 1 < 1.00 Mn,Cu,N
G 23-04 "Lean Duplex" 1.4362 GX2CrNiN23-4 0,03 23 4 <1.00 Cu,N
G 4347 1.4347 GX6CrNiN26-7 0,06 26 7 - N
G 4460 1.4460 GX3CrNiMoN27-5-2 0,03 27 5 2 N
G 4463 1.4463 GX6CrNiMo24-8-2 0,06 24 8 2
G 4468 1.4468 GX2CrNiMoN25-6-3 0,03 25 6 3 N
G 4469 1.4469 GX2CrNiMoN26-7-4 0,03 26 7 4 N 5A
G 4470 1.4470 GX2CrNiMoN22-5-3 0,03 22 5 3 N 4A
G 4517 1.4517 GX3CrNiMoCuN25-6-3-3 0,03 25 6 3 Cu,N
"Centralloy® /Märker®" Material No. Short name Analysis / Guide values in % ≈ASTM
C Cr Ni Mo Miscellaneous
G 4011 1.4011 GX12Cr12 0,12 12,00 - - -
G 4027 1.4027 GX20Cr14 0,20 14,00 - - -
G 4008 1.4008 GX7CrNiMo12-1 0,07 12,00 1,50 0,5 - CA15
G 4107 1.4107 GX8CrNi12 0,08 12,00 1,15 - -
G 4317 1.4317 GX4CrNi13-4 0,04 13,00 4,00 - - CA6NM
G 4405 1.4405 GX4CrNiMo16-5-1 0,04 16,00 5,00 1 - -
G 4036 1.4036 GX46Cr13 0,46 13,00 - - - CA40
G 4059 1.4059 GX22CrNi17 0,22 17,00 1,50 - - CB30
"Centralloy® /Märker®" Material No. Short name Analysis / Guide values in % ≈ASTM
C Cr Ni Mo Miscellaneous
G 4308 1.4308 GX5CrNi18-10 0,05 18,00 10,00 - - CF 8
G 4309 1.4309 GX2CrNi19-11 0,02 19,00 11,00 - - CF3
G 4408 1.4408 GX5CrNiMo19-11-2 0,05 19,00 11,00 2 - CF8M
G 4409 1.4409 GX2CrNiMo19-11-2 0,02 19,00 11,00 2 - CF3M
G 4552 1.4552 GX5CrNiNb19-11 0,05 19,00 11,00 - Nb ≥ x %C CF8C
G 4581 1.4581 GX5CrNiMoNb19-11-2 0,05 19,00 11,00 2 Nb ≥ x %C
G 4458 1.4458 GX2NiCrMo28-20-2 0,02 20,00 28,00 2 Cu,N
G 4416 1.4416 GX2NiCrMoN25-20-5 0,02 20,00 25,00 5 N
G 4588 1.4588 GX2NiCrMoCuN25-20-6 0,02 20,00 25,00 6 Cu,N
G 4557 1.4557 GX2CrNiMoCuN20-18-6 0,02 20,00 18,00 6 Cu,N
G 4565S (1.4565) GX3CrNiMoN24-17-5 0,03 24,00 17,00 5 N
Alloy 31 (1.4562) GXNiCrMoCuN31-27-6 0,02 27,00 31,00 6 Cu,N
"Centralloy® /Märker®" Material No. Short name Analysis / Guide values in % ≈ASTM
C Cr Ni Mo Miscellaneous
G 4559 1.4559 GX7NiCrMoCuNB41-20 0,05 20 41 4 Cu
G 45 Mo G-NiCr35MoCuN 0,02 35 45 9,5 Cu,N,others
Alloy 59 2.4605 G-NiCr23Mo16 0,01 23 Rest 16 CX2M
EUZ G 60 2.4697 G-NiCr20Mo15 0,02 19,5 Rest 15,5 Fe ≤ 2% (CW 12M)

S+C manufacturing processes in comparison.

Static casting Investment casting Vertical centrifugal casting Horizontal centrifugal casting
Outer Ø 30mm - 2,000mm - 150mm - 1,800mm 50mm - 1,300mm (Single raw casting without machining)
Length 30mm - 4,500mm 500mm - 5,550mm (for Ø1,300mm the length is max. 1,520mm)
Width 30mm - 2.000mm 500mm - -
Height 1,700mm 400mm 150mm - 1. 700mm -
Weight (operational/finished) 5,600kg / 3,000kg 0.005kg - 45kg *In single production 80kg 6,000kg 6,000kg
Maximum speed/ -G-force* - - 600rpm / 180G 1,200rpm / 140G
**1G corresponds to 1 times the acceleration due to gravity. The G-force in the centrifugal casting process acts on the solidifying steel through rotation and influences the microstructure formation during solidification towards better mechanical values. Gases and unwanted inclusions are driven to the inner diameter and can be easily removed by mechanical processing.
schmidt-und-clemens-gmbh-und-co-kg-kontakt-xxl-image.jpg

Let's talk about your requirements.

Our solutions for the steel industry. We have the perfect solution for your requirement.

Axel Korb

Area Sales Manager - Western Europe | Special Products

a.korb@schmidt-clemens.de +49 2266 92-417